Ultrasonic Piezoelectric Transducer Keramik Ring

Ultrasonic Piezoelectric Transducer Keramik Ring

Ultrasonic Piezoelectric Transducer Keramik Hringur 200kHz Ultrasonic Piezoelectric Transducer Keramik Hringur OD50.45mm * ID9.28mm 200KHZ Barium Titanat Piezo keramik diskur fiskur finnandi Piezo Ultrasonic piezoelectric transducer keramik hringur paramter: Demension: Φ50.45mm × Φ9.28mm Fm (KHz): 200KHz ± 3KHz C ...
DaH jaw

Nánari upplýsingar

Ultrasonic Piezoelectric Transducer Keramik Ring

200kHz Ultrasonic Piezoelectric Transducer Keramik Hringur OD50.45mm * ID9.28mm 200KHZ Barium Titanat Piezo keramik diskur fiskur finnandi Piezo

Ultrasonic piezoelectric transducer keramik hringur paramter:

Parameter Φ50.45mm × Φ9.28mm
Fm (KHz) 200KHz ± 3KHz
C (pF) 1650 ± 10%
R (Ω) <>
d33 ≥140
δF > 6.5k
tg ≤0,7%


QQ Myndir 20180703111938.png

Fasa umbreytingar hegðun og piezoelectric eiginleika (Na0.5K0.5) NbO3-LiNbO3 keramik

Lead-free piezoelectric keramik (1-x) (Na0.5K0.5) NbO3-xLiNbO3 {[Lix (Na0.5K0.5) 1-x] NbO3} (x = 0,04-0,20) hefur verið syntetískt með venjulegum sintering tækni. Efnið með perovskite uppbyggingu er orthorhombic fasa við x⩽0.05 og verður tetragonal fas við x⩾0.07, fasa K3Li2Nb5O15 með tetragonal wolfram brons uppbyggingu byrjar að birtast á x = 0,08 og verður ríkjandi með því að auka innihald LiNbO3. Mörkþrýstingsfasamörk milli orthorhombic og tetragonal fasa er að finna í samsetningarsvæðinu 0,05 <> Samanburður við Pb (Zr, Ti) O3, eru piezoelectric og electromechanical eiginleika aukin fyrir samsetningar nálægt morphotropic fasa mörk. Piezoelectric constant d33 gildi ná 200-235pC / N. Rafmagnsfræðilegir stuðlar í planarham og þykktarhamurinn nær 38% -44% og 44% -48%, í sömu röð. Curie hitastigið (TC) af [Lix (Na0.5K0.5) 1-x] NbO3 (x = 0,04-0,20) er á bilinu 452-510 ° C, að minnsta kosti 100 ° C hærra en venjulegt Pb (Zr, Ti) O3.